Aluminum single crystals were cyclically deformed in single-slip at small strain amplitudes
at 77 K to presaturation. The observed mechanical behavior is consistent with other
recent work. The dislocation substructure was analyzed in detail. The structure can be
described as consisting of dense bundles or veins of dislocation dipoles, separated...
The structural and stress changes in molybdenum/amorphous silicon (Mo/a-Si)
EUV reflecting multilayers during annealing at 316°C were studied. The amorphous
interlayers, with an Mo:Si stoichiometry of 1:2, grew during annealing. The residual
stresses in each component of the multilayer also changed significantly. Through high
resolution electron microscopy, selected area electron...
Part I discusses the development of an aluminum-magnesium-silicon alloy that may combine strength, extrudability, favorable corrosion resistance with low cost and scrap compatibility. The first part of the study determined the effects of small composition, heat treatment and mechanical processing changes on the ambient temperature tensile properties of the alloy....
Zirconium press plates have been developed for the production of melamine coated particle board, using shot-peening to achieve the desired plate (and therefore coated particle board) surface texture. Service temperatures of the press plates approach 200°C. This study examined the microstructural effects of extended exposure of shot-peened zirconium to temperatures...
Dwell time low cycle fatigue (DLCF), low cycle fatigue (LCF), and creep tests were performed at ambient temperature on Ti-6Al-2Sn-4Zr-2Mo-0.1Si (Ti-6242Si). Test specimens were solution annealed at various temperatures below the beta transus to control the volume fraction of primary alpha. The influence of the changes in primary alpha phase...
Silver interlayers between maraging steel base metal were examined to evaluate mechanisms leading to ductile failure in constrained thin metals. The constraint of the maraging steel base metal during uniaxial testing of constrained thin silver results in a large hydrostatic tension component, a small von Mises effective stress, and negligible...
A study of potentiostatic and galvanostatic electrochemical etching of silicon in tetramethylammonium hydroxide (TMAH) has been carried out. In TMAH baths,, we find that biased (100) silicon etch rates increase 21% over OCP etch rates. For TMAH baths seasoned with silicon, biased silicon etch rates increase to 63% over those...
Due to the aluminum industry demands, a large effort has recently been devoted to the development of special alloys to be used as inert anodes for a newly designed aluminum reduction cell. The implementation of this new technology aims at the replacement of the graphite anodes that have been used...