The fracture toughness is a critical material property that determines engineering performance.
However, as is well known for crystalline materials, if certain sample geometry and size
requirements are not met, test results become sample-size dependent and difficult to compare
among different studies. Here, the room-temperature fracture toughness of the Zr-based...
The fracture toughness is a critical material property that determines engineering performance.
However, as is well known for crystalline materials, if certain sample geometry and size
requirements are not met, test results become sample-size dependent and difficult to compare
among different studies. Here, the room-temperature fracture toughness of the Zr-based...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...