We have measured voltage-current characteristics for YBa₂Cu₃O₇ thin films in magnetic fields from 5
T to ambient, including some in the millitesla range. In all cases, the resistivity —current density isotherms
can be separated into two classes: those which exhibit upward curvature, and have constant
resistivity at low currents, and...
Transparent films of CuScO₂₊ₓ have been prepared which show p-type electrical conductivity. The temperature dependence of the conductivity indicates semiconducting behavior with an apparent room temperature activation energy of 0.11 eV. The highest room temperature conductivity observed was 30 S cm⁻1. Films 110 nm thick show 40% transparency in most...
We demonstrate color shifting from the yellow to the red in the electroluminescence from (ZnGa)S:Mn films. We observe threshold voltages down to about 35 V, extremely low for such devices. We discuss the materials characteristics of the phosphor films, and the potential for improvement of the luminous intensity of the...
High electron mobility thin films of In₂₋ₓWₓO₃₊y(0≤x≤0.075) were prepared on amorphous SiO₂ and single-crystal yttria-stablized zirconia (001) substrates by pulsed laser deposition. Mobilities ranged between 66 and 112 cm² /Vs depending on the substrate type and deposition conditions, and the highest mobility was observed at a W-dopant concentration of x~0.03....