The reaction conditions for the synthesis of Cu-BTC (BTC = benzene-1,3,5-tricarboxylic acid) were elucidated using a continuous-flow microreactor-assisted solvothermal system to achieve crystal size and phase control. A high-rate synthesis of Cu-BTC metal-organic frameworks with BET surface area of more than 1600 m²/g (Langmuir surface area of more than 2000...
The reaction conditions for the synthesis of Cu-BTC (BTC = benzene-1,3,5-tricarboxylic acid) were elucidated using a continuous-flow microreactor-assisted solvothermal system to achieve crystal size and phase control. A high-rate synthesis of Cu-BTC metal-organic frameworks with BET surface area of more than 1600 m²/g (Langmuir surface area of more than 2000...
The metal organic framework, MOF-74(Ni), was synthesized in a continuous flow microwave-assisted reactor obtaining a high space-time yield (~90 g h⁻¹ L⁻¹) and 96.5% conversion of reagents. Separation of the nucleation and growth steps was performed by using uniform and rapid microwave heating to induce nucleation, which allowed a substantial...
The reaction conditions for the synthesis of Cu-BTC (BTC = benzene-1,3,5-tricarboxylic acid) were elucidated using a continuous-flow microreactor-assisted solvothermal system to achieve crystal size and phase control. A high-rate synthesis of Cu-BTC metal-organic frameworks with BET surface area of more than 1600 m²/g (Langmuir surface area of more than 2000...
Magnesiothermic reduction can directly convert SiO₂ into Si nanostructures. Despite intense efforts, efficient fabrication of highly nanoporous silicon by Mg still remains a significant challenge due to the exothermic reaction nature. By employing table salt (NaCl) as a heat scavenger for the magnesiothermic reduction, we demonstrate an effective route to...