Phase Separation in Lean-Grade Duplex Stainless Steel 2101 Public Deposited

http://ir.library.oregonstate.edu/concern/articles/k643b320n

To the best of our knowledge, one or more authors of this paper were federal employees when contributing to this work. This is the publisher’s final pdf. The article is copyrighted by Minerals, Metals and Materials Society and published by Springer. It can be found at:  http://link.springer.com/journal/11837

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • The use of duplex stainless steels (DSS) in nuclear power generation systems is limited by thermal instability that leads to embrittlement in the temperature range of 204°C to 538°C. New lean-grade alloys, such as 2101, offer the potential to mitigate these effects. Thermal embrittlement was quantified through impact toughness and hardness testing on samples of alloy 2101 after aging at 427°C for various durations (1–10,000 h). Additionally, atom probe tomography (APT) was utilized in order to observe the kinetics of α–α′ separation and G-phase formation. Mechanical testing and APT data for two other DSS alloys, 2003 and 2205, were used as a reference to 2101. The results show that alloy 2101 exhibits superior performance compared to the standard-grade DSS alloy 2205 but inferior to the lean-grade alloy 2003 in mechanical testing. APT data demonstrate that the degree of α–α′ separation found in alloy 2101 closely resembles that of 2205 and greatly exceeds 2003. Additionally, contrary to what was observed in 2003, 2101 demonstrated G-phase like precipitates after long aging times, although precipitates were not as abundant as was observed in 2205.
Resource Type
DOI
Date Available
Date Issued
Citation
  • Garfinkel, D. A., Poplawsky, J. D., Guo, W., Young, G. A., & Tucker, J. D. (2015). Phase Separation in Lean-Grade Duplex Stainless Steel 2101. JOM Journal of the Minerals, Metals and Materials Society, 67(10), 2216-2222. doi:10.1007/s11837-015-1581-7
Series
Rights Statement
Funding Statement (additional comments about funding)
Publisher
Peer Reviewed
Language
Replaces
Additional Information
  • description.provenance : Submitted by Patricia Black (patricia.black@oregonstate.edu) on 2015-10-12T16:49:28Z No. of bitstreams: 1 GarfinkelDavidMechIndustManufEnginPhaseSeperationLean.pdf: 1887719 bytes, checksum: 7172ac0b02d94c16b5b50a52df021956 (MD5)
  • description.provenance : Made available in DSpace on 2015-10-12T16:49:55Z (GMT). No. of bitstreams: 1 GarfinkelDavidMechIndustManufEnginPhaseSeperationLean.pdf: 1887719 bytes, checksum: 7172ac0b02d94c16b5b50a52df021956 (MD5) Previous issue date: 2015-10
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2015-10-12T16:49:54Z (GMT) No. of bitstreams: 1 GarfinkelDavidMechIndustManufEnginPhaseSeperationLean.pdf: 1887719 bytes, checksum: 7172ac0b02d94c16b5b50a52df021956 (MD5)

Relationships

In Administrative Set:
Last modified: 07/27/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items