Microstructure damage of titanium films by irradiation with fission fragments Public Deposited

http://ir.library.oregonstate.edu/concern/defaults/tm70mw50g

To the best of our knowledge, one or more authors of this paper were federal employees when contributing to this work. This is the publisher’s final pdf. The published article is copyrighted by Elsevier and can be found at:  http://www.elsevier.com/.

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • Radiation damage caused by fission fragments to metal surfaces is an important research topic. Thin titanium foils were irradiated with a continuous wave beam of 132 MeV ¹³²Xe+²⁹ at the current intensity of 2 pnA. Pre- and post-irradiated surface topologies were investigated using atomic force microscopy and the observed defects were quantified by root mean square roughness, depth profile of the disordered zones, size and areal density of the voids, and discussed as a function of the applied fluencies (1– 9) 10¹³ Xe/cm². The first ellipsoidal dislocation loops appeared at the fluence of 3.0 10¹³ Xe/cm² with the areal density of 1.56 10⁶/cm² that increased to 2.0 10⁷ cm ⁻² when the dose rose to 9.0 10¹³ Xe/ cm2. At this point also the first dislocation lines with the density of 1.3 10⁷ cm ⁻² were seen. Our results suggest that the fission fragments might maximize large voids and dislocations and increase the degradation in depth resolution.
Resource Type
DOI
Date Available
Date Issued
Citation
  • Sadi, S., Paulenova, A., Loveland, W., Watson, P., Greene, J., & Zinkann, G. (2011). Microstructure damage of titanium films by irradiation with fission fragments. Nuclear Instruments & Methods in Physics Research Section B-Beam Interactions with Materials and Atoms, 269(24), 3230-3232. doi: 10.1016/j.nimb.2011.04.093
Series
Keyword
Rights Statement
Publisher
Peer Reviewed
Language
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Deborah Campbell(deborah.campbell@oregonstate.edu) on 2013-01-28T22:39:49Z (GMT) No. of bitstreams: 1 SadiSNuclearEngineeringRadiationHealthPhysicsMicrostructureDamageTitanium.pdf: 271489 bytes, checksum: d3eb9689947203b0caa6a8243599f71e (MD5)
  • description.provenance : Made available in DSpace on 2013-01-28T22:39:49Z (GMT). No. of bitstreams: 1 SadiSNuclearEngineeringRadiationHealthPhysicsMicrostructureDamageTitanium.pdf: 271489 bytes, checksum: d3eb9689947203b0caa6a8243599f71e (MD5) Previous issue date: 2011-04-22
  • description.provenance : Submitted by Deborah Campbell (deborah.campbell@oregonstate.edu) on 2013-01-28T20:20:18Z No. of bitstreams: 1 SadiSNuclearEngineeringRadiationHealthPhysicsMicrostructureDamageTitanium.pdf: 271489 bytes, checksum: d3eb9689947203b0caa6a8243599f71e (MD5)

Relationships

In Administrative Set:
Last modified: 07/17/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items