Thermal Cycling Effects on the Thermoelectric Properties of n-Type In,Ce-Based Skutterudite Compounds Público Deposited

Contenido Descargable

Descargar PDF
https://ir.library.oregonstate.edu/concern/articles/ws859g305

Descriptions

Attribute NameValues
Creator
Abstract
  • n-Type In-filled CoSb₃ is a known skutterudite compound that has shown promising thermoelectric (TE) properties resulting in high dimensionless figure of merit values at elevated temperatures. Use in various waste heat recovery applications will require survival and operation after exposure to harsh thermal cycling environments. This research focused on uncovering the thermal cycling effects on TE properties of n-type In₀.₂Co₄Sb₁₂ and In₀.₂Ce₀.₁₅Co₄Sb₁₂ skutterudite compositions as well as quantifying their temperature-dependent structural properties (elastic modulus, shear modulus, and Poisson's ratio). It was observed that the Seebeck coefficient and resistivity increased only slightly in the double-filled In,Ce skutterudite materials upon thermal cycling. In the In-filled skutterudites the Seebeck coefficient remained approximately the same on thermal cycling, while the electrical resistivity increased significantly after thermal cycling. Results also show that the thermal conductivity marginally decreases in the case of In-filled skutterudites, whereas the reduction is more pronounced in In,Ce-based skutterudite compounds. The possible reason for this kind of reduction can be attributed to grain pinning effects due to formation of nanoinclusions. High-temperature structural property measurements (i.e., Young's modulus and shear modulus) are also reported. The results show that these structural properties decrease slowly as temperature increases and that the compounds are structurally stable after numerous (up to 200) thermal cycles.
  • Keywords: Ce-based skutterudites, Thermoelectric, Structural properties, In, Thermal cycling
  • Keywords: Ce-based skutterudites, Thermoelectric, Structural properties, In, Thermal cycling
Resource Type
DOI
Fecha Disponible
Fecha de Emisión
Citation
  • Biswas, K., Subramanian, M. A., Good, M. S., Roberts, K. C., & Hendricks, T. J. (2012). Thermal cycling effects on the thermoelectric properties of n -type in,ce-based skutterudite compounds. Journal of Electronic Materials, 41(6), 1615-1621. doi: 10.1007/s11664-012-1975-z
Journal Title
Journal Volume
  • 41
Journal Issue/Number
  • 6
Academic Affiliation
Declaración de derechos
Publisher
Peer Reviewed
Language
Replaces

Relaciones

Parents:

This work has no parents.

Elementos