Nanostructured ZnO as Biomimetic Anti-reflective Coatings on Textured Silicon Using a Continuous Solution Process Public Deposited

http://ir.library.oregonstate.edu/concern/defaults/x346d9319

This is the author's peer-reviewed final manuscript, as accepted by the publisher. The published article is copyrighted by The Royal Society of Chemistry and can be found at:  http://pubs.rsc.org/en/journals/journalissues/jm#!issueid=jm022043&type=archive.

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • A novel table-top, microreactor-assisted nanomaterial deposition (MAND™) process, which combines the merits of microreaction technology with solution-phase nanomaterial synthesis and film deposition, was used to grow a nanostructured ZnO anti-reflective coating on a textured silicon substrate from aqueous solution. The subwavelength, anti-reflective nanostructures mimicked the structure and performance of the surface of the eye from a night-flying moth. Solution-processed Ag nanoparticles were applied as a seed layer on the textured silicon surface leading to preferred heterogeneous nucleation and good area coverage. Preferential growth of the nanostructured ZnO was controlled by changing residence time, reaction temperature, and concentration of precursor solution without the use of a buffer reagent (e.g. HMTA). Well-aligned ZnO nanorod arrays were fabricated by MAND at a very high depostion rate (i.e 125 nm/min) compared to batch hydrothremal method. The surface reflection of the polished silicon was suppressed from an average of 30.8% between wavelengths of 400 and 900 nm to 10.6% after micro-scale pyramidal surface texturing to 3.4% after application of the ZnO nanostructure on the textured silicon. The results provide a potential economical path to broadband anti-reflection (AR) for silicon wafers and solar cell substrates.
Resource Type
DOI
Date Available
Date Issued
Citation
  • Han, S., Paul, B., & Chang, C. (2012). Nanostructured ZnO as biomimetic anti-reflective coatings on textured silicon using a continuous solution process. Journal of Materials Chemistry, 22(43), 22906-22912. doi: 10.1039/c2jm33462c
Series
Rights Statement
Funding Statement (additional comments about funding)
Publisher
Peer Reviewed
Language
Replaces

Relationships

Parents:

This work has no parents.

Last modified

Downloadable Content

Download PDF

Items