Electromechanical strain in Bi(Zn1/2Ti1/2)O3–(Bi1/2Na1/2)TiO3–(Bi1/2K1/2)TiO3 solid solutions Public Deposited

http://ir.library.oregonstate.edu/concern/defaults/z029p5350

This is the publisher’s final pdf. The published article is copyrighted by American Institute of Physics and can be found at:  http://jap.aip.org/.

Descriptions

Attribute NameValues
Alternative Title
Creator
Abstract or Summary
  • Solid solutions ceramics of the Bi(Zn0.5Ti0.5)O-3-(Bi0.5K0.5)TiO3-(Bi0.5Na0.5)TiO3 ternary system for <20 mol. % BZT were created and confirmed to be single phase using x-ray diffraction. The dielectric dispersion showed decreasing T-max of the dielectric spectrum with a broadening of the transition with increasing BZT content. At 2.5BZT-40BKT-57.5BNT, a secondary transition commonly observed for morphotropic phase boundary (MPB) BNT-BKT was observed. The ferroelectric behavior of the system was characterized by a transition where the polarization hysteresis showed a severe pinching effect on remanent polarization (20.8 mu C/cm(2) at 2.5% BZT) as BZT contents was increased (P-r = 2.3 mu C/cm(2) at 20% BZT). Similarly, as the temperature increased to 175 degrees C, the remanent polarization of the 2.5% BZT composition significantly reduced to 2.1 mu C/cm(2). The onset of this transition corresponds to the lower temperature frequency dispersion observed in the dielectric spectrum. The strain hysteresis experienced analogous transition to the polarization, with a change in shape from typical ferroelectric butterfly to a complete loss of negative strain as BZT concentration increased. Maximum strain values of 0.33% were observed at 5-40-55 accompanied by a large d(33)* = 547 pm/V. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4714346]
Resource Type
DOI
Date Available
Date Issued
Citation
  • Patterson, E., Cann, D., Pokorny, J., & Reaney, I. (2012). Electromechanical strain in bi(Zn1/2Ti1/2)O-3-(Bi1/2Na1/2)TiO3-(Bi1/2K1/2)TiO3 solid solutions. Journal of Applied Physics, 111(9) doi: 10.1063/1.4714346
Series
Keyword
Rights Statement
Publisher
Language
Replaces
Additional Information
  • description.provenance : Made available in DSpace on 2012-07-30T17:57:04Z (GMT). No. of bitstreams: 1 CannDavidPMechanicalIndustrialManufacturingEngineeringElectromechanicalStrainBI.pdf: 2159543 bytes, checksum: bf6c48ca04cab0709016864d773fbed5 (MD5) Previous issue date: 2012-05-01
  • description.provenance : Approved for entry into archive by Deborah Campbell(deborah.campbell@oregonstate.edu) on 2012-07-30T17:57:04Z (GMT) No. of bitstreams: 1 CannDavidPMechanicalIndustrialManufacturingEngineeringElectromechanicalStrainBI.pdf: 2159543 bytes, checksum: bf6c48ca04cab0709016864d773fbed5 (MD5)
  • description.provenance : Submitted by Deborah Campbell (deborah.campbell@oregonstate.edu) on 2012-07-30T16:26:12Z No. of bitstreams: 1 CannDavidPMechanicalIndustrialManufacturingEngineeringElectromechanicalStrainBI.pdf: 2159543 bytes, checksum: bf6c48ca04cab0709016864d773fbed5 (MD5)

Relationships

In Administrative Set:
Last modified: 07/08/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items