Metallurgy and superconductivity of niobium-titanium-tantalum ternary alloy systems Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/0k225d442

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • The metallurgy and superconductivity of the Nb-Ti-Ta ternary alloy system were studied. The Nb-Ti, and Ta-Ti binary samples, and Nb-Ti-Ta ternary samples were precipitation heat treated under different schedules. After the precipitating heat treatment, the samples were characterized by X-Ray Diffraction (XRD) techniques. Equilibrium binary and ternary phase diagrams based on the different alloy compositions and heat treatment temperatures were developed. The Ta-Ti binary phase diagram is very close to the ASM standard phase diagram. The β-phase boundary of Nb-Ti binary phase diagram developed here is at a higher temperature relative to the ASM standard one. A working ternary equilibrium phase diagram for the Nb-Ti-Ta system has been developed that is based on the experimental measurements and quantitative thermodynamic calculations. Measurements of superconducting critical temperature, Tc, show a good agreement with previous measurements of Tc in the ternary alloys.
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome) using ScandAll PRO 1.8.1 on a Fi-6670 in PDF format. CVista PdfCompressor 4.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-08-15T19:35:20Z (GMT) No. of bitstreams: 1 LiNa2002.pdf: 719114 bytes, checksum: abe2aa6384820a7904af7b5aa3e17c23 (MD5)
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-08-15T19:37:28Z (GMT) No. of bitstreams: 1 LiNa2002.pdf: 719114 bytes, checksum: abe2aa6384820a7904af7b5aa3e17c23 (MD5)
  • description.provenance : Submitted by Sergio Trujillo (jstscanner@gmail.com) on 2012-08-14T19:26:26Z No. of bitstreams: 1 LiNa2002.pdf: 719114 bytes, checksum: abe2aa6384820a7904af7b5aa3e17c23 (MD5)
  • description.provenance : Made available in DSpace on 2012-08-15T19:37:28Z (GMT). No. of bitstreams: 1 LiNa2002.pdf: 719114 bytes, checksum: abe2aa6384820a7904af7b5aa3e17c23 (MD5) Previous issue date: 2001-04-13

Relationships

In Administrative Set:
Last modified: 08/03/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items