Transport properties of CuSc₁₋(subscript x)Mg(subscript x)O₂₊(subscript y) and BaCu₂S₂ transparent semiconductors

Public Deposited

Downloadable Content

Download PDF
https://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/37720h81w

Descriptions

Attribute NameValues
Creator
Abstract
  • Bulk properties of CuSc₁₋ₓMgₓO₂, CuSc₁₋ₓMgₓO₂₊y, BaCu₂S₂, Bai₁₋ₓKCu₂S₂, BaCu₂Se₂ and Bai₁₋ₓKₓCu₂Se₂ are investigated supporting the search for highly conductive p-type thin films. Mg is an efficient dopant in CuScO₂ with conductivity up to l.5.10⁻² S/cm. Oxidation of CuScO₂:Mg leads to further increase in conductivity up to 0.5 S/cm. The amount of oxygen entering the material is dependent on the Mg content with an observed maximum of y=0.23 in the 5 at. % Mg doped sample. Mg doping above 6 at. % leads to saturated or slightly decreased conductivities in CuScO₂. In the case of BaCu₂S₂:K and BaCu₂Se₂:K, conductivities of 420 S/cm and 740 S/cm are achieved at room temperature with 10 at. % potassium doping with no observable saturation, 2 orders of magnitude higher than in the corresponding undoped forms. A change from activated to metallic type conduction mechanism is observed in Bai₁₋ₓKCu₂S₂ at x>0.005. The Seebeck effect measurements demonstrate p-type conductivity for all samples. The temperature dependence of the Seebeck coefficient exhibits hopping type transport for CuSc₁₋ₓMgₓO₂₊y and metallic type for BaCu₂S₂:K. The optical properties of the 2H polymorph of CuScO₂ and CuScO₂:Mg show introduction of defects into the material compared to the 3R polymorph, and a change in color from light gray for 3R to dark gray for 2H CuScO₂:Mg was observed. Potassium doping and preparation temperature converts α-BaCu₂S₂ to β-BaCu₂S₂ which results in a change of measured band gap from 2.3 eV to 1.8 eV.
License
Resource Type
Date Available
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Publisher
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome, 8-bit Grayscale, 24-bit Color) using ScandAll PRO 1.8.1 on a Fi-6670A in PDF format. CVista PdfCompressor 4.0 was used for pdf compression and textual OCR.
Replaces

Relationships

Parents:

This work has no parents.

In Collection:

Items