Large-strain softening of aluminum in shear at elevated temperature Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/41687k47j

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • Pure aluminum deformed in torsion (shear) at elevated temperatures reaches a broad "peak" stress and then undergoes about a 17% decrease in flow stress with deformation to roughly 1-2 equivalent uniaxial strain. Beyond this strain the flow stress is approximately constant. The sources for this softening are unclear. The suggested basis includes texture softening, microstructural softening, and enhanced dynamic recovery. Experiments were performed where specimens were deformed in torsion to various strains within the softening regime followed by compression tests at ambient and elevated temperature. Analysis of the compressive yield strengths indicate that the softening is at least substantially explained by a decrease in the average Taylor factor due to the development of texture.
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Committee Member
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome, 256 Grayscale, 24-bit Color) using Capture Perfect 3.0.82 on a Canon DR-9080C in PDF format. CVista PdfCompressor 4.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-06-04T16:08:18Z (GMT) No. of bitstreams: 1 AlhajeriSalehN2002.pdf: 3933001 bytes, checksum: e2b99e308902a05aae24362fbbb051ab (MD5)
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-06-04T16:11:27Z (GMT) No. of bitstreams: 1 AlhajeriSalehN2002.pdf: 3933001 bytes, checksum: e2b99e308902a05aae24362fbbb051ab (MD5)
  • description.provenance : Submitted by Eric Hepler (ehscanner@gmail.com) on 2012-05-25T00:22:22Z No. of bitstreams: 1 AlhajeriSalehN2002.pdf: 3933001 bytes, checksum: e2b99e308902a05aae24362fbbb051ab (MD5)
  • description.provenance : Made available in DSpace on 2012-06-04T16:11:27Z (GMT). No. of bitstreams: 1 AlhajeriSalehN2002.pdf: 3933001 bytes, checksum: e2b99e308902a05aae24362fbbb051ab (MD5) Previous issue date: 2002-05-02

Relationships

Parents:

This work has no parents.

Last modified

Downloadable Content

Download PDF

Items