An investigation of precipitation from solid solution in an aluminum-magnesium-silicon alloy using x-ray diffraction techniques Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/5m60qv86d

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • The thesis was an investigation into the mechanism of precipitation from solid solution in an Aluminum-0.7% Magnesium-0.6% Silicon alloy containing iron impurities. Laue x-ray diffraction patterns were obtained from solution heat treated and aged single crystal specimens in various crystallographic orientations. Precipitation related streaking was detected on some of the patterns from aged specimens. From an analysis of the streaking it was concluded that precipitate stringlets formed during the early stages of precipitation and that the stringlets were coherent with the solid solution in the <100> directions. From the experimental results it was not possible to determine the degree of strengthening due to coherency.
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi using ScandAll PRO 1.8.1 on a Fi-6770A in PDF format. CVista PdfCompressor 4.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Made available in DSpace on 2014-05-21T17:09:49Z (GMT). No. of bitstreams: 1 GuthrieJamesL1965.pdf: 1533912 bytes, checksum: 63c7e974595a0c209e26c2ae3b3c4460 (MD5) Previous issue date: 1965-05-08
  • description.provenance : Approved for entry into archive by Katy Davis(kdscannerosu@gmail.com) on 2014-05-21T17:09:49Z (GMT) No. of bitstreams: 1 GuthrieJamesL1965.pdf: 1533912 bytes, checksum: 63c7e974595a0c209e26c2ae3b3c4460 (MD5)
  • description.provenance : Submitted by Lauren Kaysen (lkscannerosu@gmail.com) on 2014-05-16T22:21:20Z No. of bitstreams: 1 GuthrieJamesL1965.pdf: 1533912 bytes, checksum: 63c7e974595a0c209e26c2ae3b3c4460 (MD5)
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2014-05-19T15:07:27Z (GMT) No. of bitstreams: 1 GuthrieJamesL1965.pdf: 1533912 bytes, checksum: 63c7e974595a0c209e26c2ae3b3c4460 (MD5)

Relationships

In Administrative Set:
Last modified: 08/16/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items