Dwell time low cycle fatigue in Ti-6242Si Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/g445cg56h

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • Dwell time low cycle fatigue (DLCF), low cycle fatigue (LCF), and creep tests were performed at ambient temperature on Ti-6Al-2Sn-4Zr-2Mo-0.1Si (Ti-6242Si). Test specimens were solution annealed at various temperatures below the beta transus to control the volume fraction of primary alpha. The influence of the changes in primary alpha phase on low cycle dwell time fatigue life were determined and compared to the conventional low cycle fatigue properties of the alloy. A dwell period significantly decreased the number of cycles to failure, but by a decreasing factor with decreasing stress. The increased primary alpha phase present associated with lower solution anneal temperatures significantly increased susceptibility to low cycle dwell time fatigue. It is believed that dwell fatigue sensitivity may be associated with cyclic, ambient temperature, time-dependent plasticity (creep).
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome, 256 Grayscale, 24-bit Color) using Capture Perfect 3.0 on a Canon DR-9050C in PDF format. CVista PdfCompressor 4.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-09-18T21:20:58Z (GMT) No. of bitstreams: 1 FaberRobynO1999.pdf: 3756169 bytes, checksum: baafbdfa66301a6982f61b37687a7fcc (MD5)
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-09-18T21:19:21Z (GMT) No. of bitstreams: 1 FaberRobynO1999.pdf: 3756169 bytes, checksum: baafbdfa66301a6982f61b37687a7fcc (MD5)
  • description.provenance : Made available in DSpace on 2012-09-18T21:20:58Z (GMT). No. of bitstreams: 1 FaberRobynO1999.pdf: 3756169 bytes, checksum: baafbdfa66301a6982f61b37687a7fcc (MD5) Previous issue date: 1998-11-20
  • description.provenance : Submitted by Kirsten Clark (kcscannerosu@gmail.com) on 2012-09-18T18:55:30Z No. of bitstreams: 1 FaberRobynO1999.pdf: 3756169 bytes, checksum: baafbdfa66301a6982f61b37687a7fcc (MD5)

Relationships

In Administrative Set:
Last modified: 08/03/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items