Time-Dependent Crack Growth Mechanisms in Alloy 617 at 800°C in Air Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/h128nk16k

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • Time-dependent crack growth mechanisms in Alloy 617 at 800°C in air were studied using compact tension samples machined in the L-T direction, cracked at temperature using an induction furnace and servo-hydraulic load frame. The application of different loading waveforms, including triangular, hold time, and sustained loading, were studied with relation to relevant crack tip parameters in order to better understand the material’s viscoplastic response to crack growth mechanisms. Fracture surfaces and crack tip profiles were examined to discover relevant relationships between transgranular cracking, void growth and coalescence, and the role of oxygen embrittlement. A transition from transgranular cracking to void coalescence was noted, and the mechanism mapped, both onto the results obtained in this work and the existing literature. Additionally, overload experiments aided in describing stress relaxation as the dominant transgranular mechanism governing crack growth below Kth, the sustained load crack growth threshold stress intensity factor, which is also reported herein.
License
Resource Type
Date Available
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Committee Member
Academic Affiliation
Non-Academic Affiliation
Keyword
Rights Statement
Publisher
Peer Reviewed
Language
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Julie Kurtz(julie.kurtz@oregonstate.edu) on 2017-06-21T15:35:51Z (GMT) No. of bitstreams: 2license_rdf: 1527 bytes, checksum: d4743a92da3ca4b8c256fdf0d7f7680f (MD5)AddisonDylanA2017.pdf: 10496271 bytes, checksum: 4e5778e477d341c47ad3e140787c6dfd (MD5)
  • description.provenance : Approved for entry into archive by Steven Van Tuyl(steve.vantuyl@oregonstate.edu) on 2017-06-26T23:13:49Z (GMT) No. of bitstreams: 2license_rdf: 1527 bytes, checksum: d4743a92da3ca4b8c256fdf0d7f7680f (MD5)AddisonDylanA2017.pdf: 10496271 bytes, checksum: 4e5778e477d341c47ad3e140787c6dfd (MD5)
  • description.provenance : Made available in DSpace on 2017-06-26T23:13:49Z (GMT). No. of bitstreams: 2license_rdf: 1527 bytes, checksum: d4743a92da3ca4b8c256fdf0d7f7680f (MD5)AddisonDylanA2017.pdf: 10496271 bytes, checksum: 4e5778e477d341c47ad3e140787c6dfd (MD5) Previous issue date: 2017-06-07
  • description.provenance : Submitted by Dylan Addison (addisond@oregonstate.edu) on 2017-06-15T20:23:30ZNo. of bitstreams: 2license_rdf: 1527 bytes, checksum: d4743a92da3ca4b8c256fdf0d7f7680f (MD5)AddisonDylanA2017.pdf: 10496271 bytes, checksum: 4e5778e477d341c47ad3e140787c6dfd (MD5)

Relationships

Parents:

This work has no parents.

Last modified

Downloadable Content

Download PDF

Items