Mechanical properties of Nb-Ti composite superconducting wires

Public Deposited

Downloadable Content

Download PDF
https://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/kk91fp20p

Descriptions

Attribute NameValues
Creator
Abstract
  • Mechanical properties of Nb-Ti composite superconducting wires were tested at room temperature. The results were analysed using simple composite theory, the rule of mixtures. The objective is to predict the mechanical properties of Nb-Ti superconducting composite wires as a function of volume ratio and geometry of the components, the composite wire size and the effect of heat treatment at final drawing wire sizes. To understand the mechanical behaviors of the Nb-Ti composite, mechanical testing of the individual composite components, Nb-Ti filament and copper matrix, was performed, and the geometry of the composite was also studied. The results indicate that for the monofilamentary composite simple composite theory with two components, Nb-Ti filament and copper matrix, can be used as the prediction of the UTS of the composite. For the multifilamentary composite three components make up the composites; a high strength Nb-Ti fiber, a low strength, high ductility bulk copper matrix and a mid-strength (between the Nb-Ti fiber's and bulk copper matrix's) interfilamentary copper matrix. After heavy cold work the UTS of Nb-Ti filaments and bulk copper matrix in the composite saturate, while the UTS of the interfilamentary copper increases as the interfilamentary spacing decreases. The UTS of the interfilamentary copper matrix as a linear function of the reciprocal of interfilamentary spacing is found. The controlling parameters in the manufacturing which determine the mechanical properties of Nb-Ti composite superconducting wires include superconductor to composite ratio, UTS of the Nb-Ti filament and copper matrix, wire final drawing size, and geometry of the composite such as size and number of the filaments, interfilamentary spacing, volume fraction of fringe and core bulk copper in multifilamentary composites.
Resource Type
Date Available
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Publisher
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome) using ScandAll PRO 1.8.1 on a Fi-6770A in PDF format. CVista PdfCompressor 5.0 was used for pdf compression and textual OCR.
Replaces

Relationships

Parents:

This work has no parents.

In Collection:

Items