The synthesis, optical, and transport properties of SnZrS₃ Pubblico Deposited

Contenuto scaricabile

Scarica il pdf
https://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/n296x3498

Descriptions

Attribute NameValues
Creator
Abstract
  • Semiconducting materials which can be ambipolarly doped are highly desirable in many electronics applications, including use as solar cell materials. SnZrS₃ is being investigated for the possibility of ambipolar doping, with potential applications as a solar cell absorber layer. This dissertation covers the synthesis of SnZrS₃ and the related compound Sn₂S₃, as well as measurements of the optical bandgap, Seebeck coeffcient, and resistivity of pressed powder pellets for these materials. A reproducible synthesis method by solid state reaction of the elements is developed for SnZrS3. Bandgaps of 1.16-1.21 eV and 1.14-1.15 eV are found for SnZrS3 and Sn2S3 respectively. SnZrS₃ and Sn₂S₃ are found to be natively p-type, with Seebeck coeffcients of +600-700 μV/K and +1000 μV/K. Pressed pellet resistivities of 13 MΩcm for SnZrS₃ and 216 kΩcm for Sn₂S3 are measured. Preliminary doping studies are also carried out.
License
Resource Type
Date Available
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Committee Member
Academic Affiliation
Non-Academic Affiliation
Subject
Dichiarazione dei diritti
Publisher
Peer Reviewed
Language
Replaces

Le relazioni

Parents:

This work has no parents.

In Collection:

Elementi