The effect of oxide impurity on the conductivity of potassium chloride Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/s4655j90q

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • Direct current conductivity measurements on KC1:O[superscript]= crystals were used to determine an enthalpy of 0.42 ev for the dissociation for anion-vacancy-oxide ion complex. The entropy of dissociation was found to be approximately -4x 10⁻⁴ev deg⁻¹. The intrinsic "activation" energy was found to be 1.91 ev as compared to 1.95 ev, the average literature value.
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome) using ScandAll PRO 1.8.1 on a Fi-6770A in PDF format. CVista PdfCompressor 5.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2014-02-03T21:26:35Z (GMT) No. of bitstreams: 1 KoutsDaberath1972.pdf: 466780 bytes, checksum: 633a8dc863acf5d8ff61d4a69b4cdf69 (MD5)
  • description.provenance : Made available in DSpace on 2014-02-10T18:05:47Z (GMT). No. of bitstreams: 1 KoutsDaberath1972.pdf: 466780 bytes, checksum: 633a8dc863acf5d8ff61d4a69b4cdf69 (MD5) Previous issue date: 1971-09-02
  • description.provenance : Approved for entry into archive by Katy Davis(kdscannerosu@gmail.com) on 2014-02-10T18:05:47Z (GMT) No. of bitstreams: 1 KoutsDaberath1972.pdf: 466780 bytes, checksum: 633a8dc863acf5d8ff61d4a69b4cdf69 (MD5)
  • description.provenance : Submitted by Madison Medley (mmscannerosu@gmail.com) on 2014-02-03T21:15:19Z No. of bitstreams: 1 KoutsDaberath1972.pdf: 466780 bytes, checksum: 633a8dc863acf5d8ff61d4a69b4cdf69 (MD5)

Relationships

In Administrative Set:
Last modified: 08/07/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items