Rotating silver-silver chloride electrode studies in gaseous chlorine environments Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/tm70mz69m

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • The mechanism of continuously chlorinated silver-silver chloride electrode performance was studied by using a wiped, rotating, partially submerged, cylindrical silver cathode. The cell performance using a zinc anode was measured, and the rate of chlorination of silver was calculated for several water saturated chlorine atmospheres. At 75°F, with a chlorine partial pressure of 1.00 atm and a rotation speed of 1.36 RPS, a current density of over 100 ma/cm², based on the 13.74 cm² submerged cathode area, was observed when the cathode polarization was 0.19 volts (versus a silver-silver chloride reference electrode). The maximum power density produced was 32 milliwatts/cm² at a current density of 70 ma/cm² under the above operating conditions. The chlorination of silver followed the linear growth equation w = 1.80 x 10⁻⁷ + 6.65 x 10⁻⁷ t, (where w is the weight of chloride formed in g-atoms/cm², and t is exposure time in seconds) during exposures of 0.2 to 2.0 seconds in a 1.00 atm water saturated chlorine atmosphere. At lower chlorine partial pressures, the growth of the chloride film was found to follow logarithmic growth equations of the form w = K₁ + K₂ 1n t.
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi using Capture Perfect 3.0 on a Canon DR-9050C in PDF format. CVista PdfCompressor 5.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2014-05-22T20:16:19Z (GMT) No. of bitstreams: 1 GurianMarshall1964.pdf: 3018053 bytes, checksum: 06e2c394c303d105ebabd81bfa394c47 (MD5)
  • description.provenance : Made available in DSpace on 2014-05-23T18:30:38Z (GMT). No. of bitstreams: 1 GurianMarshall1964.pdf: 3018053 bytes, checksum: 06e2c394c303d105ebabd81bfa394c47 (MD5) Previous issue date: 1964-02-03
  • description.provenance : Approved for entry into archive by Katy Davis(kdscannerosu@gmail.com) on 2014-05-23T18:30:38Z (GMT) No. of bitstreams: 1 GurianMarshall1964.pdf: 3018053 bytes, checksum: 06e2c394c303d105ebabd81bfa394c47 (MD5)
  • description.provenance : Submitted by Georgeann Booth (gbscannerosu@gmail.com) on 2014-05-22T20:03:07Z No. of bitstreams: 1 GurianMarshall1964.pdf: 3018053 bytes, checksum: 06e2c394c303d105ebabd81bfa394c47 (MD5)

Relationships

Parents:

This work has no parents.

Last modified

Downloadable Content

Download PDF

Items