Internal curing of high-performance concrete for bridge decks

Öffentlich Deposited

Herunterladbarer Inhalt

PDF Herunterladen
https://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/v118rh09h

Descriptions

Attribute NameValues
Creator
Abstract
  • High performance concrete (HPC) provides a long lasting, durable concrete that is typically used in bridge decks due to its low permeability, high abrasion resistance, freeze-thaw resistance and strength. However, this type of concrete is highly susceptible to the deleterious effects of both autogenous and drying shrinkage. Both types of shrinkage occur when water leaves small pores , (< 50 nm) in the paste matrix to aid in hydration or is lost to the surrounding environment. Autogenous deformation (self-desiccation) occurs as the internal relative humidity decreases due to hydration of the cementitious material. Drying (and subsequent shrinkage) occurs when water is lost to the environment and continues until the internal relative humidity is equivalent to the ambient relative humidity. Typically, the magnitude of autogenous shrinkage is less than that of drying shrinkage. These two types of shrinkage do not act independently, and the total shrinkage is the aggregation of the two shrinkage mechanisms. It is imperative to minimize the amount of shrinkage in restrained members, such as bridge decks, to reduce the cracking potential. Various methods have been researched to minimize both types of shrinkage. Two methods to that have been reported to reduce shrinkage were selected for further research; internal curing using pre-soaked lightweight fine aggregate (LWFA) and shrinkage reducing admixtures (SRAs). The purpose of this study was to determine the long-term drying shrinkage performance of these two methods while reducing the external curing duration of 14 days for new bridge deck construction as specified by the Oregon Department of Transportation. In addition to monitoring drying shrinkage, durability testing was performed on concrete specimens to ensure these shrinkage mitigation methods performed at levels similar to concrete with the current mixture design. Freeze-thaw testing, permeability testing and restrained drying shrinkage testing were conducted. It was concluded that the combination of SRAs and pre-soaked LWFA was the most effective method to reduce longterm drying shrinkage for all curing durations (1, 7, and 14 day). Additionally, for durability testing, it was found that the use of SRAs performed the best in freeze-thaw testing, chloride permeability and restrained shrinkage.
License
Resource Type
Date Available
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Committee Member
Academic Affiliation
Non-Academic Affiliation
Subject
Urheberrechts-Erklärung
Publisher
Peer Reviewed
Language
Replaces

Beziehungen

Parents:

This work has no parents.

In Collection:

Artikel

Miniaturansicht Titel Hochladedatum Sichtbarkeit Aktionen
file details DeboodtTylerJ2012.pdf 2017-08-08 Öffentlich Herunterladen