Rheological measurements of bulk metallic glass forming alloys above the liquidus temperature Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/v979v5896

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • A high temperature high vacuum rheometer has been designed, fabricated, and tested for the study of the steady shear viscosity for multicomponent bulk metallic glass forming alloys. This rheometer has an operating range up to 1525 K, rotational frequencies of 9.4*10⁻³-3.7*10¹ radians/s, and a calibrated viscosity range of 9.6*10⁻³ and 1.2*10² Pa*s while maintaining absolute pressures pressure < 1*10⁻⁶ mbar. Zr[subscript 41.2]Ti[subscript 13.8]Cu[subscript 10.0]Ni[subscript 12.5]Be[subscript 22.5] (Vitreloy 1) is reported. The unexpected findings of non-Newtonian behavior above the liquidus temperature were observed. Observations of shear thinning, thixotropic, and viscoelastic behaviors have been made. Our results show that Vitreloy 1 can be modeled as a power law fluid, with a power law exponent of approximately -0.5 for high shear rates. We attribute the non-Newtonian behavior to structural ordering within the melt. The technological and scientific implications for non-Newtonian behavior are discussed.
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome, 24-bit Color) using ScandAll PRO 1.8.1 on a Fi-6770A in PDF format. CVista PdfCompressor 4.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-04-24T17:24:13Z (GMT) No. of bitstreams: 1 ShawTylerA2005.pdf: 11360259 bytes, checksum: 0626c5e461b7cb27a9150b63adf0b4d8 (MD5)
  • description.provenance : Approved for entry into archive by Patricia Black(patricia.black@oregonstate.edu) on 2012-04-24T17:32:30Z (GMT) No. of bitstreams: 1 ShawTylerA2005.pdf: 11360259 bytes, checksum: 0626c5e461b7cb27a9150b63adf0b4d8 (MD5)
  • description.provenance : Submitted by Sergio Trujillo (jstscanner@gmail.com) on 2012-04-18T01:01:31Z No. of bitstreams: 1 ShawTylerA2005.pdf: 11360259 bytes, checksum: 0626c5e461b7cb27a9150b63adf0b4d8 (MD5)
  • description.provenance : Made available in DSpace on 2012-04-24T17:32:30Z (GMT). No. of bitstreams: 1 ShawTylerA2005.pdf: 11360259 bytes, checksum: 0626c5e461b7cb27a9150b63adf0b4d8 (MD5) Previous issue date: 2004-11-05

Relationships

In Administrative Set:
Last modified: 08/15/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items