Fatigue of the alloy columbium (niobium) - one percent zirconium Public Deposited

http://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/wd375z913

Descriptions

Attribute NameValues
Creator
Abstract or Summary
  • This paper is a study of the fatigue properties of the alloy columbium - one percent zirconium in reverse bending. This paper also is a design study of a satisfactory plate reverse bending fatigue specimen configuration for use with the General Electric PRB pneumatic testing machine. Selected tensile tests were also run on columbium one percent zirconium to provide reference strength data with which to compare the results of the fatigue tests. The fatigue tests showed the fatigue strength of columbium - one percent zirconium to be higher than that of pure columbium. No endurance limit was found for the alloy in the range of testing from 10⁵ to 10⁷ cycles of reverse bending. A successful reverse bending fatigue specimen was designed with a triangular constant stress region where failure occurred. Generous fillets prevented unacceptable fatigue failure in the machine grips.
Resource Type
Date Available
Date Copyright
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi using Capture Perfect 3.0 on a Canon DR-9050C in PDF format. CVista PdfCompressor 5.0 was used for pdf compression and textual OCR.
Replaces
Additional Information
  • description.provenance : Made available in DSpace on 2014-06-05T15:50:38Z (GMT). No. of bitstreams: 1 WatsonWilliamP1964.pdf: 873365 bytes, checksum: d444b4e32f9e0b74b62611d2122aa8b1 (MD5) Previous issue date: 1964-05-08
  • description.provenance : Approved for entry into archive by Katy Davis(kdscannerosu@gmail.com) on 2014-06-02T19:22:01Z (GMT) No. of bitstreams: 1 WatsonWilliamP1964.pdf: 873365 bytes, checksum: d444b4e32f9e0b74b62611d2122aa8b1 (MD5)
  • description.provenance : Approved for entry into archive by Katy Davis(kdscannerosu@gmail.com) on 2014-06-05T15:50:38Z (GMT) No. of bitstreams: 1 WatsonWilliamP1964.pdf: 873365 bytes, checksum: d444b4e32f9e0b74b62611d2122aa8b1 (MD5)
  • description.provenance : Submitted by Madison Medley (mmscannerosu@gmail.com) on 2014-06-02T18:59:51Z No. of bitstreams: 1 WatsonWilliamP1964.pdf: 873365 bytes, checksum: d444b4e32f9e0b74b62611d2122aa8b1 (MD5)

Relationships

In Administrative Set:
Last modified: 08/09/2017

Downloadable Content

Download PDF
Citations:

EndNote | Zotero | Mendeley

Items