Effects of sonic, boiling, and steaming pretreatments on the drying of Pacific madrone

Public Deposited

Downloadable Content

Download PDF
https://ir.library.oregonstate.edu/concern/graduate_thesis_or_dissertations/x633f2983

Descriptions

Attribute NameValues
Creator
Abstract
  • Sonic, boiling, and steaming pretreatments were analyzed to determine their effects on radial and longitudinal liquid permeability, drying rate, and the overall dimensional change of Pacific madrone during kiln drying. Twelve days of drying at temperatures ranging from 110 °F to 140 °F and seven days of equalization were used to dry 1-inch by 1-inch Pacific madrone from green to 12 % MC. A paired comparison t-test showed that two hours of steaming increases the radial permeability of Pacific madrone, while sonic and boiling treatments did not affect permeability. Drying rate was significantly increased after two hours of sonic treatment at 15,400 Hz and also this treatment tended to make permeability and moisture content more homogeneous among the samples. Significant reductions of 33% and 27% were observed on the overall dimensional change after boiling and steaming treatment, respectively, compared to samples dried without pretreatment. Industrial application of a steaming treatment to increase radial permeability and reduce the overall dimensional change would be possible and practical for Pacific madrone. Although a reduction of drying rate occurred after steaming, it could be improved by controlling steam pressure and steam temperature.
Resource Type
Date Available
Date Issued
Degree Level
Degree Name
Degree Field
Degree Grantor
Commencement Year
Advisor
Academic Affiliation
Non-Academic Affiliation
Subject
Rights Statement
Publisher
Peer Reviewed
Language
Digitization Specifications
  • File scanned at 300 ppi (Monochrome, 8-bit Grayscale, 24-bit Color) using ScandAll PRO 1.8.1 on a Fi-6670 in PDF format. CVista PdfCompressor 4.0 was used for pdf compression and textual OCR.
Replaces

Relationships

Parents:

This work has no parents.

In Collection:

Items