Examination of Dielectric Properties of BaTiO3-SrTiO3 Based Systems Público Deposited

Conteúdo disponível para baixar

Baixar PDF
https://ir.library.oregonstate.edu/concern/honors_college_theses/0g354n334

Header

Attribute Name LabelAttribute Values Label
Creator
Abstract
  • This thesis examines the dielectric properties of two systems based on the perovskite materials barium titanate and strontium titanate. A solid solution was created starting with these base materials and then adding varying amounts of bismuth-zinc titanate and sodium niobate. These compositions were calcined and sintered at temperatures determined to be the most phasepure by x-ray diffraction. Sintered pellets were then tested using equipment to measure their capacitance as a function of temperature and their strain as a function of applied electric field. From these results and the x-ray diffraction data the lattice parameter and dielectric constant was calculated. The system with sodium niobate had the highest capacitance and dielectric constant overall. The composition with the highest capacitance, greater than 4nf at room temperature at all tested frequencies, and dielectric constant, greater than 4000 at all tested frequencies, was 68.6 mol% barium titanate, 29.4 mol% strontium titanate, and 2 mol% sodium niobate.
License Label
Resource Type
Date issued
Degree Level
Degree Name
Degree Field
Degree Grantors
Graduation Year
Contributor Advisor
Contributor Committeemember
Other Affiliation
Declaração de direitos
Publisher
Peerreviewed
Language

Relações

Relationships Parent Rows Label

Rows Empty Text

Em Collection:

Itens