The goal of this thesis is to identify and to explore novel ACTFEL phosphor
materials. Several important materials properties relevant to ACTFEL phosphor
development are identified. All of these properties cannot be obtained simultaneously.
Therefore, several key phosphor materials properties are identified as critical to the
development of an ACTFEL...
The aim of this dissertation is to develop non-traditional approaches to alternating-current thin-film electroluminescent (ACTFEL) device fabrication. ACTFEL technology suffers from a lack of adequately bright and efficient primary-color phosphors and cannot presently compete in the low-cost display market. Therefore the research presented in this dissertation focuses on an exploration...
The aim of the research undertaken for this thesis was to develop a new high-performance amorphous oxide semiconductor (AOS) for use as a channel layer in a thin-film transistor (TFT). AOS TFTs offer higher electron mobility than the established amorphous silicon based technology. A new channel material comprised of aluminum...
CIGS and CdTe based commercial thin-film solar cells (TFSCs) require an absorber thickness greater than 2 µm and 4 µm, respectively, to adequately absorb the solar spectrum. To efficiently extract photoexcited electrons, these TFSCs require relatively defect-free absorbers with high-minority carrier mobility (> 100 cm2V−1s−1) and long lifetime (> 10...
The aim of this dissertation is to develop oxide semiconductors by radio-frequency
sputtering for thin-film transistor (TFT) applications. A variety of oxide semiconductors
are used as the TFT channel layer, including indium gallium oxide (IGO), zinc tin
oxide (ZTO), and indium gallium zinc oxide (IGZO). The variety of materials used...
Current cadmium telluride and copper indium gallium diselenide thin-film solar cells
(TFSCs) utilize thick absorbers (2 - 4 μm). For efficient carrier extraction in these TFSCs,
the absorber layer requires high carrier mobilities and a long minority carrier lifetime, which
necessitates the use of a high purity, defect-free thin film....
Due to a lack of grain boundaries, an amorphous metal thin film (AMTF) possesses advantageous mechanical properties and enhanced chemical stability that is potentially useful for thermal inkjet (TIJ) printing applications. The use of an AMTF as a TIJ resistor or cavitation plate could lead to a thinner TIJ cavitation...
The goal of this thesis is the identification and synthesis of high-luminance,
primary color alternating-current thin-film electroluminescent (ACTFEL) devices.
Special attention is paid to the synthesis of primary color green ACTFEL devices because
of the lack of an adequate primary green ACTFEL phosphor and the dominance
of green wavelengths in...