p-type conducting films of α- BaCu₂S₂ have been deposited onto glass and KBr substrates, yielding a conductivity of 17 S/cm and a Hall mobility of 3.5 cm²/Vs. For a 430-nm-thick film, the optical transparency approaches 90% in the visible portion of the spectrum at 650 nm, and a transparency of...
In situ photoemission spectroscopy experiments are used to characterize the interface between ZnTe and the wide band gap p-type semiconductor BaCuSeF. The contact is characterized by a null valence-band offset, a large conduction-band offset, and a chemically graded interface. By applying the transitivity rule for band offset and on the...
BaCuQF (Q=S,Se) materials, candidate transparent p-type conductors, were prepared by solid-state reaction, and their bulk electrical and optical properties were evaluated. The room-temperature Seebeck coefficient and electrical conductivity of undoped BaCuQF pellets were +56 μV/K and 0.088 S/cm, respectively, for the sulfide fluoride, and +32 μV/K and 0.061 S/cm, respectively,...
The origin of high hole conduction in BaCuQF (Q=S,Se) was investigated by photoemission
measurements and full-potential linearized augmented plane wave band-structure calculations. In
both compounds, the large dispersion near the top of the valence band is realized by admixed states
of Cu 3d and S 3p or Se 4p orbitals,...
Transparent thin-film transistors (TTFTs) with an amorphous zinc tin oxide channel layer formed via rf magnetron sputter deposition are demonstrated. Field-effect mobilities of 5–15 and 20–50 cm² V‾¹ s‾¹ are obtained for devices post-deposition annealed at 300 and 600 °C, respectively. TTFTs processed at 300 and 600 °C yield devices...
High electron mobility thin films of In₂₋ₓWₓO₃₊y(0≤x≤0.075) were prepared on amorphous SiO₂ and single-crystal yttria-stablized zirconia (001) substrates by pulsed laser deposition. Mobilities ranged between 66 and 112 cm² /Vs depending on the substrate type and deposition conditions, and the highest mobility was observed at a W-dopant concentration of x~0.03....
BaCuChF (Ch=S,Se,Te) surfaces and BaCuSeF interfaces with zinc phthalocyanine (ZnPc) were studied by photoelectron spectroscopy. BaCuChF compounds oxidize when exposed to ambient atmosphere. Se capping layers were studied as a means to produce representative surfaces for photoelectron spectroscopic measurements. Decapped BaCuSeF surfaces remain O-free and C-free when the Se layer...