This study investigated the effect of exposure to elevated temperature on the yield strength of single-shear nail connections when subjected to lateral loading. Solid sawn lumber and laminated veneer lumber were used as framing members and two different thicknesses of both oriented strand board and plywood were used as the...
The construction industry has relied heavily on wood and wood-based composites, such as oriented strand board (OSB) and plywood for timber frame construction. Therefore, it is highly imperative to categorize the response of wood-based composites when exposed to elevated temperatures for a sustained period of time. The essence of fire-resistant...
Wood and wood-based composites are being used extensively in single-family residential dwellings. Therefore, it is important to categorize their response when exposed to elevated temperatures for a sustained period of time. In fire-resistant design for wood structures, the main goal is to ensure that enough structural integrity is maintained, during...
Wood and wood-based composites are being used extensively in single-family residential dwellings. Therefore, it is important to categorize their response when exposed to elevated temperatures for a sustained period of time. In fire-resistant design for wood structures, the main goal is to ensure that enough structural integrity is maintained, during...
Engineers, in practice, are often faced with the challenge of evaluating a fire-damaged structure and developing a rehabilitation and retrofit plan. In order to decide on a rehabilitation and retrofit plan, information on thermal degradation of building materials and connections are vital. A critical knowledge gap exists in terms of...
Fracture toughness of wood and wood composites has traditionally been characterized by a stress intensity factor, an initiation strain energy release rate (G[subscript init]) or a total energy to fracture (G[subscript f]). These parameters provide incomplete fracture characterization for these materials because the toughness changes as the crack propagates. Thus...
Wood I-joists are often left uncovered and exposed to the weather during construction, allowing the oriented strandboard and laminated veneer lumber in these systems to be adversely affected by water absorption. Manufacturers typically specify that these materials be protected from wetting, but this can be difficult in wetter climates. There...
To quantify the postpeak residual capacity and
to gain insights into the load transfer mechanism of a shear
wall, nail connection tests were performed on salvaged
connections after a monotonic shear wall test loaded up
to peak load. Experimental results reveal that there is a
loss of strength in most...
Fracture toughness of wood and wood composites has traditionally been characterized by a stress intensity factor, an initiation strain energy release rate (G init) or a total energy to fracture (G f). These parameters provide incomplete fracture characterization for these materials because the toughness changes as the crack propagates. Thus,...
Residential energy use is a significant contributor to greenhouse gas emissions and climate change. Reducing energy efficiency in conventional wood-framed houses are thermal bridges: direct paths that allow heat to flow through the studs instead of the insulation. One suggestion for reducing thermal bridging is the staggered stud (SS) wall....