The fracture toughness is a critical material property that determines engineering performance.
However, as is well known for crystalline materials, if certain sample geometry and size
requirements are not met, test results become sample-size dependent and difficult to compare
among different studies. Here, the room-temperature fracture toughness of the Zr-based...
The fracture toughness is a critical material property that determines engineering performance.
However, as is well known for crystalline materials, if certain sample geometry and size
requirements are not met, test results become sample-size dependent and difficult to compare
among different studies. Here, the room-temperature fracture toughness of the Zr-based...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...
Bulk metallic glasses (BMGs) have been reported to have large variability in mode I fracture toughness. In this study, alternating soft and hard regions were created in a Zr₅₂.₅Ti₅Cu₁₈Ni₁₄.₅Al₁₀ (at%) BMG via mechanical imprinting at room temperature. While only 50% of as-cast samples demonstrated plastic deformation during mode I fracture...
OBJECTIVES: Secondary caries is the most common reason for composite restoration replacement and usually forms between dentin and the filling. The objective of this study was to investigate the combined effect of cyclic loading and bacterial exposure on bacterial penetration into gaps at the interface between dentin and resin composite...
The fatigue crack growth rates for nickel-based superalloy Haynes 282 were measured at temperatures of 550, 650, and 750 °C using compact tension specimens with a load ratio of 0.1 and cyclic loading frequencies of 25 Hz and 0.25 Hz. Increasing the temperature from 550 to 750 °C caused the...
The fracture toughness is a critical material property that determines engineering performance.
However, as is well known for crystalline materials, if certain sample geometry and size
requirements are not met, test results become sample-size dependent and difficult to compare
among different studies. Here, the room-temperature fracture toughness of the Zr-based...
The slow β relaxation is understood to be a universal feature of glassy dynamics. Its presence in bulk metallic
glasses (BMGs) is evidence of a broad relaxation time spectrum that extends to deep within the glassy state.
Despite the breadth of research devoted to this phenomenon, its microscopic origin is...
OBJECTIVES. Bioactive glass (BAG) is known to possess antimicrobial properties and release ions needed for remineralization of tooth tissue, and therefore may be a strategic additive for dental restorative materials. The objective of this study was to develop BAG containing dental restorative composites with adequate mechanical properties comparable to successful...
Interstitially filled skutterudites are a promising class of state-of-the-art thermoelectric
materials. Although thermoelectrics are exposed to significant thermal stresses, little
information is known about the fracture toughness of interstitially doped skutterudites. This
work explores the fracture toughness of undoped Co₄Sb₁₂ and indium doped In₀.₁Co₄Sb₁₂
skutterudites using three methods: 1) Vickers...
Small crack fatigue is a widely recognized problem in the fatigue of materials; however, there has been limited progress in developing methods for predicting small crack fatigue behavior. In this paper, small crack effects due to crack bridging are addressed. A fatigue threshold R-curve was measured for a 99.5% pure...