Corrosion of reinforcement is recognized as the predominant factor that limits the service life of reinforced concrete (RC) structures exposed to aggressive environments. This corrosion deterioration can lead to damage resulting in capacity loss or even failure. For structures exposed to coastal marine environments or deicing or anti-icing applications, this...
The production of cement and concrete results in the production of large amounts of CO₂ emissions which can have significant negative environmental impacts. Using supplementary cementing materials (SCMs) as a cement replacement is an effective solution to reduce these negative environmental impacts, as most SCMs are waste by-products from other...
:
________________________________________________________________________
DavidTrejo
The production of cement and concrete results in the production of large amounts
The research presented in this thesis assessed the use of high strength steel (HSS) reinforcement for use in reinforced concrete (RC) bridge columns. HSS is not currently allowed in reinforced concrete bridge columns due to a lack of information on the material characteristics and performance information when used in RC...
Most specifications for ready-mix concrete (RMC) limit mixing time to 90 minutes and/or truck drum revolution counts (DRC) to 300 before discharge. These specifications have been in place for many years with the objective of ensuring the quality and performance of the finished concrete product. However, limited research has been...
Cast-in-drilled-hole (CIDH) piles are often constructed to depths that are inaccessible to internal vibration of the concrete. Internal vibration is necessary to consolidate the concrete and, if not performed, then typically inspection pipes are necessary to detect the presence of voids in CIDH piles. Void detection is critical to assessing...
Use of high-strength steel (HSS) reinforcing bars could provide constructability and economic benefits for the construction of structures, reducing the initial and ultimately the life-cycle cost of bridge and building structural elements. This thesis summarizes work performed in a research project on the use of HSS reinforcing bars for concrete...
Alkali silica reaction (ASR) and corrosion of reinforcement are two deterioration mechanisms in reinforced concrete (RC) structures. These deterioration mechanisms can significantly damage a RC structure and reduce its service life. Supplementary cementitious materials (SCMs) are commonly used to improve the durability of RC systems containing reactive aggregate that are...
Concrete is the most widely used construction material in the world. When constructing large concrete structures, concrete may have to be placed in multiple lifts. In these cases, fresh concrete is placed on hardened concrete. The interface that is formed between these two lifts of concrete is known as a...
Significant progress has been made over the past 20 years in developing models to estimate the service-life of reinforced concrete systems. The basic understandings of the mechanisms that control the transport of ions and moisture in concrete systems have been well researched and models for determining corrosion initiation, specifically chloride-induced...
The use of high strength steel reinforcement has the potential to provide economic and constructability benefits when used in reinforced concrete structures. However, more research is needed to justify and confidently allow its use. Current design provisions limit the nominal yield strength of reinforcing steel bars to 60 ksi (420...